home

Hammer

Print Back content list

Hammer

last updated : 2019/03/19

Code	Description	Budget Price	Ship. weight	Ship. vol.
ETOOHAMMCARP	HAMMER, nail claw, carpenter type, 800g, steel + plast. hand	CH 14.30	0kg	0	Add

ETOOHAMMCARW	CLAW HAMMER, carpenter type, 750g, wood handle	on request	0kg	0	Add

ETOOHAMMRI03	HAMMER, standard, hardened steel, wood handle, 300g	CH 3.80	0.4kg	0,7875L	Add

ETOOHAMMRI05	HAMMER, standard, hardened steel, wood handle, 500g	CH 4.50	0.6kg	1,152L	Add

ETOOHAMMRI15	HAMMER, standard, hardened steel, wood handle, 1500g	CH 9.20	1.78kg	2,128L	Add

ETOOHAMMSL10	SLEDGE HAMMER, hardened steel, wood handle, 1200g, 250mm	CH 9.10	0kg	0	Add

ETOOHAMMSL17	SLEDGE HAMMER, hardened steel, wood handle, 1750g, 250mm	CH 13.70	1.6kg	1,54L	Add

ETOOHAMMSL48	SLEDGE HAMMER, hardened steel, wood handle, 4800g, 900mm	CH 25.20	5.4kg	0,01008m³	Add

General information

Standard hammer for carpenter and most of general building and maintenance work.

Specifications

CLAW HAMMER
Type	Carpenter hammer, head and handle. One side flat, one side claw.
Material	High-carbon steel head, treated to achieve a martensitic structure, with dressed striking faces.
Quality of make	No dents, no cracks, smooth surface and edges. No excess metal in the eye.
Weight of the head	750g +/- 1%
Rockwell hardness C (HRC)	50 minimum to 58 maximum on striking faces.
Rockwell hardness C (HRC)	35 maximum closed to the eye.
Applicable standard	ISO15601.
Handle: No chips, rough surfaces, holes, or knots. Smooth polished varnished surface. Dry, strong, and flexible wood. Handle adjusted to head in order to protrude on other side of the head, and be blocked with a metal wedge. Moisture minimum 10%, maximum 15%, under ISO3130.
Pull apart test: After two series of 25 vigorous blows with varying delivery angle, apply a traction of minimum 50kg trying to pull out the handle, head being fixed in a jaw, this should not create any damage to the hammer head and the handle, and the handle should remain firmly attached to the head.
Bending test: For claw hammer only, apply a load perpendicularly to the axis of the handle and close to the end, so as to obtain a 125 N.m torque, irrespective of the size of the hammer. The load shall start at zero and be applied gradually, without jerking. The test load shall be held for at least 10s. This should not create any damage the hammer head and handle.